AJ Fibertek India’s insulation division offers high-performance solutions built for extreme heat and noise environments. Our HAMAT® range—made from ECR glass and high-silica fibers—is trusted in automotive exhaust systems, industrial equipment, and power applications. Lightweight, non-combustible, and customizable, our insulation products meet stringent emission and performance standards while improving efficiency and durability across critical systems.
ECR-Glass Needle Mats are made from 100 % inorganic fiber and are non-combustible with high porosity and excellent sound absorption.
| Technical Characteristics | |
|---|---|
| Material | E-Glass |
| Transformation Temp | 640°C |
| Filament Diameter | 9-13 um |
| Ignition Loss | ≤ 2.0% |
| Volume Shrinkage | 0% |
| Density (Kg/m3) | 120 ~ 160 |
| Thickness (mm) | 3 ~ 20 |
| Combustibility | Non-Combustible |
| Binder | Binder Free |
ECR-Glass Needle Mats are made from 100 % inorganic fiber and are non-combustible with high porosity and excellent sound absorption.
| Technical Characteristics | |
|---|---|
| Material | ECR-Glass |
| Transformation Temp | 761°C |
| Filament Diameter | 13-19 um |
| Ignition Loss | ≤ 2.0% |
| Volume Shrinkage | ≤ 1 % |
| Density (Kg/m3) | 120 ~ 160 |
| Thickness (mm) | 3 ~ 20 |
| Combustibility | Non-Combustible |
| Binder | Binder Free |
High Silica Needle Mats are made from 100 % inorganic fiber and are non-combustible with high porosity and excellent sound absorption.
| Technical Characteristics | |
|---|---|
| Material | Silica Fiber |
| Transformation Temp | 850°C |
| Filament Diameter | 7-16 um |
| Ignition Loss | ≤ 9.0 % |
| Volume Shrinkage | ≤ 8 % |
| Density (Kg/m3) | 120 ~ 160 |
| Thickness (mm) | 3 ~ 20 |
| Combustibility | Non-Combustible |
| Binder | Binder Free |
Silica Needle Mats are 100% inorganic fiber, non-combustibility with high porosity, excellent sound absorption. Special features with high temperature duration, low heat shrinkage and heat loss. As well as low thermal conductivity, excellent thermal insulation and good tensile strength and resistance for wind velocity.
| Technical Characteristics | |
|---|---|
| Material | High Silica Fiber |
| Transformation Temp | 1050°C |
| Filament Diameter | > 6 um |
| Ignition Loss | ≤ 9% |
| Volume Shrinkage | Max 7 % |
| Density (Kg/m3) | 120 ~ 160 |
| Thickness (mm) | 3 ~ 20 |
| Combustibility | Non-Combustible |
| Binder | Binder Free |
Our experience team is ready to assist you with your custom insulation, tooling or implant needs. Contact us now!